RTV-2 silicone Liquid is generally named as two-part room-temperature vulcanized silicone rubber, which features exceptional fluidity and good operability. When mixed with 2-3% curing agent, they can still be operated within 30-40 minutes but will be formed after 4-6 hours. With resistance to deformation, high temperature, acid and alkali, and expansion.
PRODUCT FEATURES
1. Good flow ability and long working time
2. Excellent performance for duplication
3. High tear and tensile strength
4. Easy de-mould from complex replica parts
5. Acid and alkali-resistance
6. Low linear shrinkage
| Ratio of Catalyst | Pot Life | Cure Time |
|---|---|---|
| 4% (4g per 100g) | 4-6 minutes | 1.5 – 2.5 hours |
| 3% (3g per 100g) | 15-20 minutes | 3-5 hours |
| 2% (2g per 100g) | 25-30 minutes | 7-10 hours |
Technical Data (approx values)
soft Shore A 25/ Viscosity 22000-250000
Cure: 4- 6 Hrs.
USING INSTRUCTION
1-Take 100g of part A and add 2g of part B catalyst and mix the silicone rubber and curing agent evenly in the container stirring and making sure not to incorporate air..
2-vacuum pumping may be applied
3-Pouring into a mold or block mold of silicone rubber
The pouring way is an easy way such as a long treacle to fill molds, it’s slowly . Allow to set.
or creating a two-part mold or molding a glass object a release agent is required.
Can be pigmented to a wide range of colors It can be softened to your own requirements using this softening additive Can be made thixotropic for applying to vertical surfaces or to over head objects
SUITABLE FOR USE WITH
Polyurethane resin *
(* Excl. some transparent polyurethanes, check with the supplier of the resin if silicone molds are suitable.)
Epoxy resin *
(* Excl. some epoxies, check with the supplier of the resin if silicone molds are suitable.)
Polyester resin
Acrylic resin
Plastisol (PVC)
Plaster
Cement
Polymer Clays
Waxes
Soaps
Metals with a pouring temperature below 180°C
not Suitable for use with food .
Catalyst Irritant see IFU.